Name : Hot rolled tool Steel plate AISI A2, cold drawn steel bar, Forged Die Steel SKD21
Special use : Mold Steel, Free Cutting Steel, Model Steel
Application : Tool Steel Bar, Die Steel Bar, Structural Steel Bar, industry, Cold work tool steel
Surface treatment : black or machined, Black Bright Mirror(mill Polishing HL Etc), black surface or mi
Dimensions : 15-300MM, Dia 2mm~1500mm, Round50--1000mm, 20~600mm, Dia 50mm-430mm
Delivery condition : Peeled, EAF+LF+VD, Finish Machining, Q+T, annealed or QT.
A2 COLD WORK TOOL STEEL, SPECIAL STEEL, DIE STEEL/SKD12/1.2363A2 DIE STEEL, SPECIAL STEEL, COLD WORK STEEL
Heat treatment Related
Slowly heated the A2 steel material to 650-680°C (1202-1256°F) before raising the temperature to 1050-1100°C (1922-2120°F) and soak A2 tool steel material until uniformly heated. Initial hammer blows should be light due to the comparatively high hot strength of this steel.
The A2 steel forged temperature should be maintained above 1000°C(1832℉) until the A2 steel metal begins to yield. Final forged should not be done below 900°C(1652℉). Slowly cool after forged is essential to avoid the possibility of cracking.
Slowly heated A2 steel to 850-870 ℃(1562-1598°F) and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace at a rate of 4°C (40°F) per hour or less.. The A2 tool steel will get MAX 250 HB (Brinell hardness).
A2 steels should be heated uniformly to 790-820°C (1436-1508°F) until completely heated through. Then heated to the hardening temperature of 950-980°C(1742-1796℉), soak at the temperature enough time, let A2 steel to be thoroughly heated .
Then withdraw A2 steel tools from the furnace,either air cool or oil quench.
Tempering of A2 tool steel
Tempering of A2 steels is performed at 150-400°C (302-752°F), Soak well at the selected temperature and soak for at least one hour per 25mm of total thickness. Get Rockwell C hardness of 57 to 62. Others different Heat treatment temperature will get different hardness. Below only for reference.
Temperature [℃] 150 200 250 300 350 400
Hardness [HRc] 62-61 61-60 60-59 59-58 58-57 58-57
A2 SKD12 1.2363A2 Special Cold Work Die Steel Images